Product name: |
titanium forged ring |
Material: |
Gr5 |
Application: |
Chemical industry |
Outer diameter: |
200-1300mm |
Inner diameter: |
100-900mm |
Height: |
35-250mm |
Thickness: |
40-400mm |
Quality control: |
Ultrasonic Testing |
Product name: |
titanium forged ring |
Material: |
Gr5 |
Application: |
Chemical industry |
Outer diameter: |
200-1300mm |
Inner diameter: |
100-900mm |
Height: |
35-250mm |
Thickness: |
40-400mm |
Quality control: |
Ultrasonic Testing |
Seamless Rolled Titanium Ring Titanium Forged Ring Titanium Forgings
Low density and high strength.
Corrosion resistance,
acid and alkali resistance,
high temperature resistance,
low temperature resistance.
Good welding performance,
mechanical processing performance,
heat exchange performance and air suction performance.
It is non-magnetic,
has memory function,
superconducting function,
and does not interact with the human body.
Seamless Rolled Titanium Ring also referred to as seamless forged rings are starting blank products that go through additional forming, machining and grinding in order to produce finished components. In most cases, its production involves a process called ring rolling on rolling mills that vary in size. Through this process, parts can be manufactured to tight tolerances and specific geometries that come with outstanding surface smoothness and concentricity. Forged ring products can have an outside diameter of a few inches like the smallest washer-ring to much larger parts that are over 9 feet in diameter.
The ring rolling process starts with a circular preform of metal that has been previously upset and pierced (using the open die forging process) to form a hollow “doughnut.” This doughnut is heated above the recrystallization temperature and placed over the idler or mandrel roll. This idler roll then moves under pressure toward a drive roll that continuously rotates to reduce the wall thickness, thereby increasing the diameters (I.D. and O.D.) of the resulting ring.
Chemical requirements | |||||||||||
N | C | H | Fe | O | Al | V | Pd | Mo | Ni | Ti | |
Gr1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18 | / | / | / | / | / | bal |
Gr2 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | / | / | bal |
Gr5 | 0.05 | 0.08 | 0.015 | 0.40 | 0.20 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
Gr7 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
Gr12 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |